Stanyl® HFX61S
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P17Oi1_StanylHFX61S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl®HFX61S is a polyamide 46 (nylon 46) material, which contains a 35% glass fiber reinforced material. This product is available in the Asia-Pacific region,. Stanyl®The main features of HFX61S are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.49 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.1 | -- | % | ISO 294-4 |
| Flow | 0.40 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11500 | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | 3.1 | % | ISO 527-2 |
| Flexural Modulus | 10500 | 8000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 285 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ||||
| Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Flow | 1.7E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Lateral | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec (0.180 mm) | 120 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.40 | 11.0 | IEC 60250 | |
| 1 MHz | 4.10 | 5.00 | IEC 60250 | |
| 1.00 GHz | 3.90 | 4.10 | IEC 60250 | |
| 10.0 GHz | 3.80 | 4.00 | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.180 mm | V-0 | -- | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 300 - 310 | °C | |
| Middle Temperature | 305 - 315 | °C | |
| Front Temperature | 310 - 320 | °C | |
| Nozzle Temperature | 315 - 325 | °C | |
| Processing (Melt) Temp | 320 - 330 | °C | |
| Mold Temperature | 100 - 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 - 3.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® E 8940SG | Vyncolit N.V. | Epoxy | Vyncolit® |
| ALAMID® 6.6 GF 30 MOD WL SCHWARZ-9665 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| LUVOCOM® 1-3260/schwarz | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| MAJ'ECO EP287W | AD majoris | PP Copolymer | MAJ'ECO |
| Plexar® PX2246 | LyondellBasell Industries | HDPE | Plexar® |