OXPEKK® Permetta™ Film SP
| Category: | PEKK , Polyetherketoneketone |
| Manufacturer: | Oxford Performance Materials, Inc. |
| Trademark: | OXPEKK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P0r1Iv_OXPEKK-Permetta-Film-SP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (380°C/8.4 kg) | 35 to 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | < 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Break 1 | 11.9 | MPa | |
| Break 2 | 17.9 | MPa | |
| Break | 89.6 | MPa | |
| Break 3 | 6.96 | MPa | |
| Break 4 | 9.51 | MPa | |
| Break 5 | 10.5 | MPa | |
| Tensile Elongation (Break) | 80 | % | ASTM D638 |
| Flexural Modulus | 3380 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 138 | MPa | ASTM D790 |
| Compressive Strength | 103 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Itself - Static) | 0.29 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 141 | °C | ASTM D648 |
| Glass Transition Temperature | 154 | °C | DSC |
| Melting Temperature | 303 | °C | DSC |
| CLTE - Flow (< 154°C) | 7.7E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 75 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 2.10 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Stainless Steel |
| 2 . | Steel |
| 3 . | Galvanized Steel |
| 4 . | Aluminum |
| 5 . | Anodized Aluminum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYNE® ABS CBE 75 | Tyne Plastics LLC. | ABS | TYNE® ABS |
| Latilub 30/R-07 GRT | LATI S.p.A. | PS (GPPS) | Latilub |
| Karina WHITE PVC COMPOUND -E 830-10/189-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ NF001 compound | SABIC Innovative Plastics | PC+ABS | LNP™ THERMOCOMP™ |
| PHOENIX™ 2301 | Phon Tech Industrial Company | SEBS | PHOENIX™ |