Tufpet PBT G1010 is a Polybutylene Terephthalate (PBT) material filled with 10% glass fiber. It is available in North America for injection molding. Important attributes of Tufpet PBT G1010 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 78.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 3920 | MPa | ASTM D790 |
| Flexural Strength | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Unnotched Izod Impact | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 200 | °C | ASTM D648 |
| RTI Elec | UL 746 | ||
| 0.760 mm | 75.0 | °C | |
| 1.57 mm | 75.0 | °C | |
| 3.18 mm | 75.0 | °C | |
| RTI Imp | UL 746 | ||
| 0.760 mm | 75.0 | °C | |
| 1.57 mm | 75.0 | °C | |
| 3.18 mm | 75.0 | °C | |
| RTI Str | UL 746 | ||
| 0.760 mm | 75.0 | °C | |
| 1.57 mm | 75.0 | °C | |
| 3.18 mm | 75.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.760 mm | HB | ||
| 1.57 mm | HB | ||
| 3.18 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 to 303 | °C | |
| Middle Temperature | 230 to 303 | °C | |
| Front Temperature | 230 to 303 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9740 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| PROTEQ™ H2US | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| TechnoDur PBT 4 GF10 black (9991) | TechnoCompound GmbH | PBT | TechnoDur |
| Borealis PP RA130E-1498 | Borealis AG | PP Random Copolymer | Borealis PP |
| ESENTTIA 03H83A | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |