WanBlend® WHT-THF9465T2
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | WanBlend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Oz5ImG_WanBlend-WHT-THF9465T2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WHT-THF9465T2 is polyester-based flame retardant thermoplastic Polyurethane (TPU) compound, supplied in form of transparent, translucent pellets, which combine the zero halogen objective with excellent mechanical properties and processability. Applications: Extrusion - wire and cable General extrusion and injection molding where flame retardant properties are required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 62 to 68 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 6.80 | MPa | |
| 300% Strain | 14.0 | MPa | |
| Tensile Strength | 34.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 650 | % | ASTM D412 |
| Tear Strength | 70.0 | kN/m | ASTM D624 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 185 | °C | |
| Middle Temperature | 195 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 205 | °C | |
| Injection Pressure | 65.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C | |
| Die Temperature | 195 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP H7700 | LG Chem Ltd. | PP Homopolymer | SEETEC PP |
| TOTAL Polypropylene PPH 9081 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| ACCUTECH™ HP0336M10CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Deltron 5311 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PPS | Deltron |
| LNP™ STAT-KON™ DEL339XF compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |