Order Products : sales@su-jiao.com
Huafon T25HP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Huafon Group Co., Ltd. |
| Trademark: | Huafon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OykgGb_Huafon-T25HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
T25 is light low viscosity resin, with good flowability. Typical Applications T25HP is mainly used for the spinning of short and long fibres, also can be used as compounding materials. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 110 | g/10 min | ISO 1133 |
| Particle Size | 1.50 to 2.10 | g/100 pellets | Internal Method |
| Relative Viscosity | 2.40 to 2.50 | Internal Method | |
| Water Content | < 5000 | mg/kg | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | 75.2 | MPa | ISO 527-2 |
| Tensile Strain 2(Break) | 67 | % | ISO 527-2 |
| Flexural Modulus 3 | 2610 | MPa | ISO 178 |
| Flexural Stress 4 | 98.5 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 5.9 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Annealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 63.1 | °C | ISO 75-2/A |
| Vicat Softening Temperature 7 | 233 | °C | ISO 306/B120 |
| Peak Melting Temperature 8 | 259 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 9 | UL 94 | ||
| 1.00 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-2 |
| Note Message | |
|---|---|
| 1 . | 48h/23°C/50%RH |
| 2 . | 48h/23°C/50%RH |
| 3 . | 48h/23°C/50%RH |
| 4 . | 48h/23°C/50%RH |
| 5 . | 48h/23°C/50%RH |
| 6 . | 48h/23°C/50%RH |
| 7 . | 48h/23°C/50%RH |
| 8 . | 10°C/min |
| 9 . | 48h/23°C/50%RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 G15 TZ NTLA010 NR374 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Clariant Nylon 6 PA213G13 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| Galloo GP-PE-0320 | Galloo Plastics | PE, Unspecified | Galloo |
| HiFill® TPU/E 0140 | Techmer Engineered Solutions | TPU, Unspecified | HiFill® |
| HiFill FR® PC GF10 FR BK | Techmer Engineered Solutions | PC | HiFill FR® |