Andur 80-5AP/Curene® 280
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Oxw85L_Andur-80-5AP-Curene-280.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| All properties based on Andur® 80-5AP cured with Curene® 280 |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 25.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 3.63 | MPa | ASTM D412 |
| 300% strain | 5.79 | MPa | ASTM D412 |
| Tear Strength | |||
| -- 1 | 52.5 | kN/m | ASTM D624 |
| Cracking | 28 | kN/m | ASTM D470 |
| Compression Set | 30 | % | ASTM D395 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 15 | min | |
| Post Cure Time (23°C) | 72 | hr |
| Additional Information |
|---|
| Prepolymer NCO%: 3.0-3.4Grams Curene® 280 per 100 grams prepolymer: 20.3Rebound, %: 60Stoichiometry: 0.95Prepolymer Temperature, °F: 190-210Curene® 280 Temperature, °F: 158Post Cure Time, 212°F, hours: 16 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 107 | °C |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 907 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Axiall PVC 19461 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Duron PEI 1000 | ProPolymers Inc. | PEI | Duron |
| EPO-TEK® 301-2 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| KMI PP KM-303IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |