Akulon® Diablo HT-HG6 (K-X07031)
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OvH08u_Akulon-Diablo-HT-HG6-K-X07031-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Akulon® Diablo HT-HG6 (K-X07031) is a Polyamide 66/6 Copolymer (Nylon 66/6) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary attribute of Akulon® Diablo HT-HG6 (K-X07031): Heat Stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.75 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.9 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9850 | 5500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.3 | 6.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | 55 | kJ/m² | |
| 23°C | 60 | 85 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 275 to 295 | °C | |
| Middle Temperature | 275 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MegaCarb® 520R | Mega Polymers | PC | MegaCarb® |
| VITAMIDE® AR3XNT6061 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| DOW™ LLDPE DNDA-7340 NT 7 | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| Bapolene® 3257U | Bamberger Polymers, Inc. | HDPE | Bapolene® |
| LubriOne™ AT-000/15T | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |