TRANSMARE® BIO 35MI-10-0.001
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® BIO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OvG2gZ_TRANSMARE-BIO-35MI-10-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® BIO 35MI-10-0.001 is a PLA INGEO™ based impact modified biopolymer with good flow and impact properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 73 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 2370 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00mm, injection molding | 42.0 | MPa | ISO 527-2/50 |
| Fracture, 4.00mm, injection molding | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00mm, injection molding | 2.4 | % | ISO 527-2/50 |
| Fracture, 4.00mm, injection molding | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus (Injection Molded) | 2380 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C, injection molding | 1.5 | kJ/m² | ISO 179/1A |
| -20°C, injection molding | 3.5 | kJ/m² | ISO 179/1A |
| 0°C, injection molding | 4.2 | kJ/m² | ISO 179/1A |
| 23°C, injection molding | 5.3 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C, injection molding | 54 | kJ/m² | ISO 179/1U |
| 23°C, injection molding | No Break | ISO 179/1U | |
| Notched Izod Impact (23°C, Injection Molded) | 5.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C, Injection Molded) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 51.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 49.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 59.0 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 195 | °C | |
| Nozzle Temperature | 205 | °C | |
| Mold Temperature | 25.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| In specific cases pre-drying of this material might be required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPV Elastoprene® N55A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Elastollan® 1190A50 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Keysor PVC KC1101 | Keysor-Century Corporation | PVC, Unspecified | Keysor PVC |
| Petrothene® NA480145 | LyondellBasell Industries | LDPE | Petrothene® |
| ULTEM™ 2110R resin | SABIC Innovative Plastics | PEI | ULTEM™ |