Generic PP Homopolymer - Mica
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ouq8h5_Generic-PP-Homopolymer---Mica.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Mica This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.971 - 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 - 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.50 - 1.3 | % | ASTM D955 |
| 23°C | 0.65 - 1.3 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 35 - 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1800 - 4140 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 30.9 - 37.2 | MPa | ASTM D638 |
| Fracture, 23°C | 26.9 - 31.1 | MPa | ASTM D638 |
| 23°C | 29.6 - 35.4 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 2.9 - 7.1 | % | ASTM D638 |
| Fracture, 23°C | 3.0 - 20 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1720 - 5340 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 35.9 - 55.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 26 - 54 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 93 - 420 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 112 - 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.2 - 91.7 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 84.2 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 205 - 233 | °C | |
| Mold Temperature | 18.3 - 65.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - MicaThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AR36RD6636 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Gallonprene® GP210-4504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| EPIMIX POM IMP NC B501 | EPSAN Plastik SAN. ve TiC. A.S. | Acetal (POM) Copolymer | EPIMIX |
| LNP™ LUBRICOMP™ LX00430 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |
| Hifax M2 U13 C11306 | LyondellBasell Industries | PP Copolymer | Hifax |