Infino LB-3150GW
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OuhsG9_Infino-LB-3150GW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High-impact resistant PC/GF material that can be used for middle mold frame of LCD TV BLU |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 26 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.40 | % | ASTM D955 |
| Ash Content | |||
| -- | 15 | % | ISO 3451 |
| -- | 15 | % | ASTM D5630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3800 | MPa | ASTM D638 |
| -- | 4000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 69.0 | MPa | ASTM D638 |
| Yield | 72.0 | MPa | ISO 527-2/50 |
| Break 3 | 69.0 | MPa | ASTM D638 |
| Break | 69.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 4.3 | % | ASTM D638 |
| Break | 4.1 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 4500 | MPa | ASTM D790 |
| -- 6 | 3800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 120 | MPa | ASTM D790 |
| -- 8 | 114 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 7.4 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 79 | J/m | ASTM D256 |
| 23°C 10 | 7.7 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 142 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 141 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/B50 |
| -- | 146 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 68.6 to 226 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA S310 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Shandong PA6 A1R02 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| TAIRIREX GP535A | Formosa Plastics Corporation | PS (GPPS) | TAIRIREX |
| TUFLIN™ HS-7066 NT 7 | The Dow Chemical Company | LLDPE | TUFLIN™ |
| LNP™ THERMOTUF™ VX00585 compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ THERMOTUF™ |