RAMTOUGH PZ333G2
| Category: | PC , Polycarbonate |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMTOUGH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OucZOY_RAMTOUGH-PZ333G2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% GLASS-FIBER REINFORCED, FLAME RETARDANT POLYCARBONATE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | 0.40 - 0.60 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 60.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 10 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2 |
| Flexural Modulus | 3400 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 120 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 90 | J/m | ASTM D256 |
| 23°C | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 265 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 265 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Processing (Melt) Temp | 270 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 70.0 - 107 | MPa | |
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9966-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| DuPure® TU 76 V | Ducor Petrochemicals BV | PP Impact Copolymer | DuPure® |
| HiFill® PA6/6 GF17 IM2 L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Hyril® GP355AS | Entec Polymers | SAN | Hyril® |
| Sylvin 9077-85 Grey 9331 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |