Fortron® ICE 506L
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OucQgo_Fortron-ICE-506L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron ICE 506L is a faster crystallizing version of Fortron 1140L6. It offers essentially the same characteristics of 1140L6 with improved crystallization efficiency for faster cycle times in complex geometries. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.60 | g/cm³ | ASTM D792 |
| -- | 1.65 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 0.20 - 0.30 | % | ASTM D955 |
| Transverse flow | 0.50 - 0.70 | % | ASTM D955 |
| Vertical flow direction | 0.40 - 0.60 | % | ISO 294-4 |
| Flow direction | 0.20 - 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Spiral Flow | 21.5 | Internal method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat Capacity of Melt | 1500 | J/kg/°C | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CSA Rating - F-1 (840.0 µm) | A00 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class m | 100 | ASTM D785 | |
| M scale | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 200 | MPa | ASTM D638 |
| Fracture | 195 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.0 | % | ASTM D638 |
| Fracture | 1.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 14500 | MPa | ISO 178 |
| Flexural Stress | 285 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 53 | kJ/m² | ISO 179/1eU |
| 23°C | 53 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 34 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 280 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 265 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 270 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 215 | °C | ISO 75-2/C |
| Glass Transition Temperature 1 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 3 | 15 | kV/mm | ASTM D149 |
| -- | 28 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 kHz | 3.50 | ASTM D150 | |
| 1 MHz | 3.50 | ASTM D150 | |
| 1 MHz | 4.10 | IEC 60250 | |
| Dissipation Factor | |||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | IEC 60250 | |
| Arc Resistance | 134 | sec | ASTM D495 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 90.0 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa | |
| Screw Speed | 50 - 120 | rpm |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE J 110 | ADDIPLAST | PP Copolymer | ADDILENE |
| Europrene Latice® 5588 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| Favorite LL565 | Favorite Plastics | LLDPE+EVA | Favorite |
| Hanwha Total PP HTB72 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Karina GRAY PVC COMPOUND 828-18/423-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |