LNP™ THERMOCOMP™ PF008 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OuU1E8_LNP-THERMOCOMP-PF008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* PF008 is a compound based on Nylon 6 resin containing 40% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PF-1008 Product reorder name: PF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.20 to 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.98 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12700 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 184 | MPa | ASTM D638 |
| Break | 186 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 3.3 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 9260 | MPa | ASTM D790 |
| -- | 9530 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 279 | MPa | ASTM D790 |
| -- | 278 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 18 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 92 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 25.1 | J | ASTM D3763 |
| -- | 21.6 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 196 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 208 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 2800 B-55A Black | RTP Company | TPV | RTP |
| Mowiol® 8-88 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| TAROMID B 280 MT5 Y2 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| ASI POLYPROPYLENE 1349 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Glastic® 1872 | Glastic Corporation | Polyester, TS | Glastic® |