| A HIGHLY FLAME RETARDED, LEAD FREE 75C DEGREE LOW SMOKE JACKETING COMPOUND FOR PLENUM CABLE CONSTRUCTIONS REQUIRING COMPLIANCE TO U.L. SUBJECT 910 MODIFIED STEINER TUNNEL TEST. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 - 1.60 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 65 - 71 | ASTM D2240 | |
| Shaw D, 15 seconds | 51 - 57 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (0.381 mm) | 17.2 | MPa | ASTM D412 |
| Tensile Elongation (fracture, 0.381mm) | 170 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -9.00 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (23°C, 100 MHz) | 3.25 | ASTM D150 | |
| Dissipation Factor (23°C, 100 MHz) | 0.014 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 47 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 | °C | |
| Cylinder Zone 2 Temp. | 154 | °C | |
| Cylinder Zone 3 Temp. | 163 | °C | |
| Cylinder Zone 4 Temp. | 168 | °C | |
| Cylinder Zone 5 Temp. | 168 | °C | |
| Adapter Temperature | 154 | °C | |
| Melt Temperature | 179 - 185 | °C | |
| Die Temperature | 154 | °C | |
| Extruder Screw Compression Ratio | 3.0:1.0 |
| Extrusion instructions |
|---|
| Melt temperature is critical, at temperatures above 370 degrees F foaming may occur. It may be necessary to adjust barrel temp to attain the desired melt temperature. Material should be dried prior to use. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 526K | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| Telcar® TL-2565A | Teknor Apex Company | TPE | Telcar® |
| EVICOM™ GI5/215 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| Ecomass® 4703ZC76 | Ecomass Technologies | TPU, Unspecified | Ecomass® |
| Lucent POM POM-900P | Lucent Polymers, Inc. | Acetal (POM) Homopolymer | Lucent POM |