Trithene® CX 8087
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Trithene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OrYQNb_Trithene-CX-8087.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trithene®CX 8087 is a medium density polyethylene material,. This product is available in Latin America and is processed by film extrusion. Trithene®The main features of CX 8087 are:
Trithene®The typical application fields of CX 8087 are: movies |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.931 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 14.0 | MPa | ASTM D638 |
| Fracture, molding | 12.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 520 | % | ASTM D638 |
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.65 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 150 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 160 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 18.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 380 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 680 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 330 | g | ASTM D1922 |
| TD : 50 µm, blown film | 230 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.0 µm, Blown Film) | 90 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 1.8 to 2.6 g/10 minDensity, ASTM D1505: 0.929 to 0.933 g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 145 - 160 | °C | |
| Cylinder Zone 2 Temp. | 155 - 170 | °C | |
| Cylinder Zone 3 Temp. | 165 - 175 | °C | |
| Adapter Temperature | 175 - 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-IM1G33 | Polymer Resources Ltd. | Nylon 66 | PRL |
| MIDILENA III PPS1001 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Task® 14 | Smooth-On, Inc | PUR, Unspecified | Task® |
| VESTOLIT® P 1982 K | VESTOLIT GmbH & Co. KG | PVC Copolymer | VESTOLIT® |
| Durethan® BG 30 X H3.0 000000 | LANXESS GmbH | Nylon 6 | Durethan® |