POLYlux 3809S
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYlux |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OrKKws_POLYlux-3809S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/PBT-Blend |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 to 1.0 | % | |
| Flow | 0.70 to 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 76 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2000 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 15 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 132 | °C | ISO 306/A50 |
| -- | 108 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V959 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Qenos PP PPU 1080 | Qenos Pty Ltd | PP Homopolymer | Qenos PP |
| RheTech Polypropylene HP521-188UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SynPlast™ L9TM-E | PolyOne Corporation | Triisononyl Trimellitate | SynPlast™ |
| Formolene® 6375N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |