TAROMID A 280 G6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OqDF3P_TAROMID-A-280-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 medium viscosity glass fiber reinforced 30%, good mechanical and thermal properties. UL94 HB approuved at 0,75 mm - NC Available: all colors, UV stabilized (L), heat stabilised (H), high heat stabilised (HT), release agent (W), improved glyco-hydrolysis stability (I). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 to 1.36 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 to 0.40 | % | |
| Across Flow | 0.90 to 1.1 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.70 | % | ASTM D570, ISO 62 |
| Saturation | 5.0 | % | ASTM D570 |
| Saturation, 23°C | 5.0 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9600 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 175 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.4 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 9200 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 250 | MPa | ISO 178 |
| Break | 250 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 8.0 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2 | ASTM D256, ISO 179 | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 244 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 3 | 100 | °C | IEC 60216 |
| -- 4 | 130 | °C | IEC 60216 |
| -- 5 | 140 | °C | IEC 60216 |
| -- 6 | 180 | °C | ASTM D794 |
| Vicat Softening Temperature | 254 | °C | ISO 306/B50, ASTM D1525 7 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 256 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 2.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 8.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 26 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | 20000 hrs |
| 4 . | Heat Stabilised & High Heat Stabilised, 20000 hrs |
| 5 . | Short Term |
| 6 . | Heat Stabilised & High Heat Stabilised, Short Term |
| 7 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 291 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Abstron SHF50+ | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Borealis LE4147 | Borealis AG | LDPE | Borealis |
| Chiao Fu PA6 MC212G20 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| ExxonMobil™ PP2252E4 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |