TAROBLEND 30
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Opy9yL_TAROBLEND-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TAROBLEND 30 is a Polycarbonate + ABS (PC+ABS) product. It can be processed by injection molding and is available in Europe. Typical application: Automotive. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 to 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.40 to 0.70 | % | |
| Flow | 0.40 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.25 | % | |
| Saturation, 23°C | 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1950 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 44.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 25 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress 2 | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 350 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 98.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 3 | 60.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 118 | °C | ISO 306/A50 |
| -- | 112 | °C | ISO 306/B50 |
| CLTE - Flow (-30 to 30°C) | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 550 | °C | IEC 60695-2-12 |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Pre-heater | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 20000 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-9640 | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| ADMER™ AT2717E | Mitsui Chemicals Europe GmbH | PP, Unspecified | ADMER™ |
| ExxonMobil™ LLDPE LL 8450 Series | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| INSPIRE™ 6022N | Braskem America Inc. | PP Homopolymer | INSPIRE™ |
| LEXAN™ 923 resin | SABIC Innovative Plastics | PC | LEXAN™ |