POLYAXIS® LP 699
| Category: | LMDPE , Linear Medium Density Polyethylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYAXIS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Opgo0z_POLYAXIS-LP-699.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Long term UV8 stabilization |
| General Information | |
|---|---|
| Additive |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.940 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.9 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, Rotational Molded) | 17.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Rotational Molded) | 400 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Rotational Molded) | 848 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength (-40°C, 3.18 mm, Rotational Molded) | 85 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Rotational Molded) | 61.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN J-550A | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| TAISOX 7320M | Formosa Plastics Corporation | EVA | TAISOX |
| Braskem PE GM5240PR | Braskem | HDPE | Braskem PE |
| Karina IVORY PVC COMP. 105908-35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYFLAM® RABS 90950 UV5 | A. Schulman Europe | ABS | POLYFLAM® |