InnoTuf® TP-4052
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OpW79r_InnoTuf-TP-4052.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TP-4052 is a rigid, impact resistant polyurethane formulated for hand-batch processing, vacuum assist casting or meter mix dispense methods Excellent physical properties can be obtained with a mild post cure without the utilization of mercury, MOCA or TDI TP-4052 is a tough ABS simulated product with a very low mixed viscosity |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.10 | g/cm³ | |
| Hardener | 1.10 | g/cm³ | |
| Base Resin | 1.16 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1550 | MPa | ASTM D790 |
| Flexural Strength | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 71.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 53 Mix Ratio by Weight: 50 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 60 to 120 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 38°C 1 | 0.40 | Pa·s | |
| 38°C 2 | 0.60 | Pa·s | |
| 38°C 3 | 1.0 | Pa·s | |
| Curing Time 4 | 26 | hr | |
| Gel Time | 5.0 to 9.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Strength | 57.9 | MPa | ASTM D638 |
| Tensile Elongation at Break | 12 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 2 hours at 150°F + 24 hours at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8891-92 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ASTALAC™ ABS X15 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Arnite® TV4 240 | DSM Engineering Plastics | PBT | Arnite® |
| GLS ABS SN08 | GLS Polymers Pvt. Ltd. | ABS | GLS ABS |
| LUVOCOM® 1105-7685 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |