Polifil® Nylon 930L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OpRL9Z_Polifil-Nylon-930L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® Nylon 6 provides superior strength and rigidity with electrical resistance and surface lubricity. These properties have been proven to work in the following applications: automotive, bearings, and appliances. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.6 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3030 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 79.3 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 8.0 | % | |
| Break, 23°C | 40 | % | |
| Flexural Modulus - Tangent (23°C) | 2690 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | 1.36 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 182 | °C | |
| 1.8 MPa, Unannealed | 62.8 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 249 | °C | |
| Middle Temperature | 271 | °C | |
| Front Temperature | 282 | °C | |
| Nozzle Temperature | 282 | °C | |
| Processing (Melt) Temp | 277 to 293 | °C | |
| Mold Temperature | 37.8 to 93.3 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SBB4710 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Clariant Nylon 6/12 612-01-L | Clariant Corporation | Nylon 612 | Clariant Nylon 6/12 |
| Elastron® G G103.A80.B | Elastron USA, Inc. | SEBS | Elastron® G |
| 3M™ Dyneon™ Fluoroelastomer FPO 3520 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| LEXAN™ HF1140R resin | SABIC Innovative Plastics | PC | LEXAN™ |