OP - PC - Filled PC BK20 8SS
| Category: | PC , Polycarbonate |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PC - Filled |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OndXOC_OP---PC---Filled-PC-BK20-8SS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMI / ESD SHIELDING |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 58.6 | MPa | ASTM D638 |
| Fracture | 58.6 | MPa | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 152 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 141 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Additional Information |
|---|
| Melt Mass- Flow Rate (MFR), ASTM D1238, 230°C/ 3.8kg: 15 to 25 g/10 minSurface Resitivity, ASTM D257: 1E1 to 1E3 ohms |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 - 121 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 288 - 293 | °C | |
| Processing (Melt) Temp | 293 - 327 | °C | |
| Mold Temperature | 82.2 - 104 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7575 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SUMIPLOY® AS1411 | Sumitomo Chemical Co., Ltd. | PESU | SUMIPLOY® |
| Vinnolit® S 3160 | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Utomer UT590 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| Aurora PVC AP3141 Series | Aurora Plastics, Inc. | PVC, Rigid | Aurora PVC |