Order Products : sales@su-jiao.com
LNP™ STAT-KON™ EE005E compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OmgXRS_LNPSTATKONEE005Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* EE005E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding. Also known as: LNP* STAT-KON* Compound EC-1005 EM Product reorder name: EE005E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.37 | g/cm³ | ASTM D792 |
| -- | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.050 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.30 - 0.50 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.10 - 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.23 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12300 | MPa | ASTM D638 |
| -- | 11700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 200 | MPa | ASTM D638 |
| Fracture | 194 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.1 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 14300 | MPa | ASTM D790 |
| -- | 15000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 278 | MPa | ASTM D790 |
| -- | 277 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| 23°C 3 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.4 | J | ASTM D3763 |
| -- | 7.14 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 207 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 208 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 - 1.0E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 354 - 366 | °C | |
| Front Temperature | 366 - 377 | °C | |
| Processing (Melt) Temp | 360 - 366 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RenPIM® VG 5289 Polyol/ 5289 Isocyanate | Huntsman Advanced Materials | PUR, Unspecified | RenPIM® |
| VITAMIDE® BR16GY6522 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Fiberfil® PP-60/TC/20/VO/ND | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| KYOCERA KE-870 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| ISPLEN® PP 086 U6E | REPSOL | PP Homopolymer | ISPLEN® |