LNP™ THERMOCOMP™ EC006AQW compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OmXydn_LNP-THERMOCOMP-EC006AQW-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* EC006AQW is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound EC006AQW Product reorder name: EC006AQW |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (380°C/6.7 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.030 - 0.10 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.10 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 29200 | MPa | ASTM D638 |
| -- | 27500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 255 | MPa | ASTM D638 |
| Fracture | 257 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 1.4 | % | ASTM D638 |
| Fracture | 1.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 22200 | MPa | ASTM D790 |
| -- 5 | 23300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 350 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 351 | MPa | ASTM D790 |
| Compressive Strength | 234 | MPa | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 81 | J/m | ASTM D256 |
| 23°C 7 | 7.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 8 | 33 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 198 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 9 | 198 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 380 - 400 | °C | |
| Middle Temperature | 380 - 400 | °C | |
| Front Temperature | 380 - 400 | °C | |
| Processing (Melt) Temp | 380 - 400 | °C | |
| Mold Temperature | 165 - 180 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Injection Speed: 40 - 70 mm/s |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2305 A | RTP Company | PUR, Unspecified | RTP |
| RABALON® MJ7301C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Karina BLACK PVC COMPOUND -E CAK 60-48/ 1-F | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Osterlene® PPH-35-.5 | Osterman & Company | PP Homopolymer | Osterlene® |
| LNP™ LUBRICOMP™ KP004L compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |