Order Products : sales@su-jiao.com
AIE PA66 60G3F
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OlR4qx_AIE-PA66-60G3F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AIE PA66 60G3F is a Polyamide 66 (Nylon 66) material filled with 15% glass fabric. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of AIE PA66 60G3F are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.80 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 123 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7100 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 16 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 265 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 50.0 to 100 | °C | |
| Injection Pressure | 30.0 to 80.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2625 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Resinoid 1371 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Sumitomo Epoxy E 8354A-2 | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| Sumikon® PM-5620 | SBHPP | Phenolic | Sumikon® |
| LNP™ THERMOCOMP™ JF004E compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |