Zytel® 73G30T NC010
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OkwpUp_Zytel-73G30T-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Toughened, Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 6.2 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.8 | -- | % | |
| Viscosity Number | 135 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9100 | 5700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 170 | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 9000 | 5700 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | 12 | kJ/m² | |
| 23°C | 20 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 100 | 94 | kJ/m² | |
| 23°C | 100 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 12 | 12 | kJ/m² | |
| 23°C | 17 | 24 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 80 | 80 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 221 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.8E-5 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 22 | -- | mm/min | ISO 3795 |
| Flammability Classification (1.50 mm) | HB | -- | IEC 60695-11-10, -20 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.31 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2200 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.23 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THORNEL® P-25 | Cytec Industries Inc. | Carbon/Epoxy | THORNEL® |
| Celcon® WR25Z | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Hanwha Total PP RP100W130 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| IZTAVIL P-440 | Mexichem Corporativo | PVC Homopolymer | IZTAVIL |
| TAFMER™ DF840 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |