Clearflex® FF 106
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OktspL_Clearflex-FF-106.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FF 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion. Film manufactured with Clearflex FF 106 are characterised by high optical properties (haze, gloss), optimum impact, tear and puncture resistance. Main Application Clearflex FF 106 is recommended for the production of blown stretch film, low gauge agricultural, in coextrusion or blending with LDPE. Because of its excellent bubble stability, Clearflex FF 106 is the ideal choice for the production of low gauge film where high mechanical properties are required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 190 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 9.00 | MPa | |
| TD : Yield, 25 µm, Blown Film | 10.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 50.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 45.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 550 | % | |
| TD : Break, 25 µm, Blown Film | 700 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 190 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 150.0 | kN/m | |
| TD : 25.0 µm | 250.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 103 | °C | ISO 306/A |
| Melting Temperature | 125 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 8.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® RGF 20 BLACK | SRF Ltd. | Nylon 66 | TUFNYL® |
| New-prene™ 8080B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Borealis PP MD231U | Borealis AG | PP Copolymer | Borealis PP |
| Alpha PVC 2235L-75 CLEAR 030X | AlphaGary | PVC, Flexible | Alpha PVC |
| ColorFast® NY2GF131 | LTL Color Compounders, Inc. | Nylon 66 | ColorFast® |