Durethan® BKV 50 H EF DUS022 900116
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OirFdv_DurethanBKV50HEFDUS022900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.57 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.70 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.070 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.20 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.020 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 16200 | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 205 | 128 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.3 | 4.3 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 15000 | 9700 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | -- | 197 | MPa | ISO 178/A |
| 23°C | 320 | 203 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 2.9 | 4.0 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-160, GF50 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy 8 | 3.60 | 5.80 | J | ISO 6603-2 |
| Film Puncture Force 9 | 1220 | 1260 | N | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 13 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 85 | 80 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 11 | -- | kJ/m² | ISO 180/1A |
| 23°C | 14 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 75 | -- | kJ/m² | ISO 180/1U |
| 23°C | 80 | 70 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 207 | -- | °C | ISO 75-2/A |
| Melting Temperature 10 | 220 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 23°C |
| 9 . | 23°C |
| 10 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-3418 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| STELACOAT FA-2500/FB-2500 | DIC Corporation | PUR, Unspecified | STELACOAT |
| Monprene® MP-2850M-UV | Teknor Apex Company | TPE | Monprene® |
| Veradel® 3500 | Solvay Specialty Polymers | PESU | Veradel® |
| Karina WHITE PVC COMPOUND 850-10/116-Y-ERYB-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |