This data represents typical values that have been calculated from all products classified as: Generic Epoxy - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 - 2.03 | g/cm³ | ASTM D792 |
| Apparent Density | 0.78 - 0.91 | g/cm³ | ASTM D1895 |
| Bulk Factor | 2.5 | ASTM D1895 | |
| Molding Shrinkage - Flow (23°C) | 0.091 - 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.079 - 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 105 - 115 | ASTM D785 | |
| Barcol Hardness | 70 - 72 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Fracture, 23°C | 70.8 - 90.8 | MPa | ASTM D638 |
| 23°C | 55.2 - 198 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 13600 - 20600 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 103 - 543 | MPa | ASTM D790 |
| Fracture, 23°C | 112 - 161 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 185 - 263 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 16 - 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, not annealed | 246 - 302 | °C | ASTM D648 |
| 1.8 MPa, annealed | 279 - 282 | °C | ASTM D648 |
| CLTE - Flow | |||
| -- | 1.4E-5 - 5.1E-5 | cm/cm/°C | ASTM D696 |
| -- | 1.4E-5 - 3.7E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (23°C) | 0.33 - 0.74 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 2.6E+13 - 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 11 - 16 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 23°C | 3.79 - 5.80 | ASTM D150 | |
| 23°C | 3.70 - 4.60 | ASTM D2520 | |
| Dissipation Factor (23°C) | 7.7E-3 - 0.020 | ASTM D150 | |
| Arc Resistance | 178 - 187 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 29 - 50 | % | ASTM D2863 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time | 7.5 - 180 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 104 - 106 | °C | |
| Mold Temperature | 162 - 163 | °C | |
| Injection Pressure | 50.5 - 51.7 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Epoxy - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3EG7 BK00564 | BASF Corporation | Nylon 6 | Ultramid® |
| 4PROP® 9C23300 | 4Plas | PP Copolymer | 4PROP® |
| COSMOTHENE® EVA H2181 | TPC, The Polyolefin Company (Singapore) Pte Ltd | EVA | COSMOTHENE® EVA |
| Sylvin 5145-75 Clear Green 3125 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8925-80 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |