Witcom PA66 3C
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ogo6fG_Witcom-PA66-3C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Witcom PA66 3C is a Polyamide 66 (Nylon 66) product filled with 15% carbon fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.50 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 7.2 | % | |
| Equilibrium, 23°C, 50% RH | 2.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 185 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 to 3.5 | % | ISO 527-2 |
| Flexural Modulus | 9300 | MPa | ISO 178 |
| Flexural Stress | 245 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| CLTE - Flow | 2.8E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 to 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 750 | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zeoforte® ZSC2395 | Zeon Corporation | NBR | Zeoforte® |
| Fluon® ETFE Film | Asahi Glass Co., Ltd. | ETFE | Fluon® |
| Iupilon® EGN2010R2 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| PERCOM® MCS12A | A. Schulman Europe | PP Copolymer | PERCOM® |
| Petrothene® YR92866 | LyondellBasell Industries | LDPE+EVA | Petrothene® |