LNP* Stat-kon* DD000P is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Exceptional Processing. Also known as: LNP* STAT-KON* Compound D- EP Product reorder name: DD000P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.84 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.74 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2490 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 57.2 | MPa | ASTM D638 |
| Yield | 57.0 | MPa | ISO 527-2 |
| Fracture | 49.6 | MPa | ASTM D638 |
| Fracture | 51.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.8 | % | ASTM D638, ISO 527-2 |
| Fracture | 20 | % | ASTM D638 |
| Fracture | 9.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Stress | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 230 | J/m | ASTM D256 |
| 23°C 2 | 21 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2200 | J/m | ASTM D4812 |
| 23°C 3 | 210 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 40.5 | J | ASTM D3763 |
| -- | 40.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 135 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 125 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 126 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.4E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 - 1.0E+9 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ RC66-BK09 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| Viprene™ G50A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Zythane® 4090A | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Adell Polyamide BL-35 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| CERTENE™ PRB-2C | Muehlstein | PP Random Copolymer | CERTENE™ |