BJB Polyurethane TC-866 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OfzKn3_BJB-Polyurethane-TC-866-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-866 A/B is a medium viscosity, economical and easy to handle two component urethane compound. This system cures relatively fast at room temperature producing tough, impact resistant castings. TC-866 A/B is recommended in applications where a resilient surface hardness is desired while maintaining good flexibility. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.15 | g/cm³ | ASTM D792 |
| -- 2 | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 3(12.7 mm) | 0.60 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 - 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 683 | MPa | ASTM D638 |
| Tensile Strength | 17.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 70 | % | ASTM D638 |
| Flexural Modulus | 640 | MPa | ASTM D790 |
| Flexural Strength | 19.8 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 102 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 95 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2393 | ||
| 25°C 4 | 1350 | cP | ASTM D2393 |
| 25°C 5 | 1500 | cP | ASTM D2393 |
| 25°C | 1400 | cP | ASTM D2393 |
| Demold Time (25°C) | > 120 | min | |
| Post Cure Time (71°C) | 16 | hr | |
| Work Time 6(25°C) | 5.0 - 6.0 | min | Internal method |
| Additional Information |
|---|
| Most of the physical properties can be achieved in 5-7 days at ambient temperature, 77°F (25°C). In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 160°F (71°C). |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | 12 x 0.5 x 0.5 in |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | 100 g mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moldex® QS985A/M151 | Mitsubishi Chemical Corporation | Polyolefin, Unspecified | Moldex® |
| Elastollan® LP 9307 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Estane® 5703 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| ICORENE® N2231 (XD00045) | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |
| LEXAN™ HFD4413 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |