Diakon® Frost 642 22
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OfOfct_Diakon-Frost-642-22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diakon®Frost 642 22 is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion or injection molding. Diakon®The main characteristics of Frost 642 22 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/1.2 kg) | 1.6 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.80 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 22 | ISO 2039-2 | |
| Ball Indentation Hardness (H 961/30) | 180 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 23 | % | ISO 527-2 |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.1 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 28 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 4.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 76.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ISO 306/A |
| -- | 84.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 75.0 | % | ASTM D1003 |
| Haze | 65 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 190 - 240 | °C | |
| Middle Temperature | 200 - 260 | °C | |
| Front Temperature | 210 - 270 | °C | |
| Nozzle Temperature | 210 - 260 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C |
| Injection instructions |
|---|
| Feed Throat: 50 to 80°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 160 - 240 | °C | |
| Cylinder Zone 2 Temp. | 180 - 250 | °C | |
| Cylinder Zone 3 Temp. | 200 - 250 | °C | |
| Cylinder Zone 4 Temp. | 220 - 260 | °C | |
| Cylinder Zone 5 Temp. | 220 - 270 | °C | |
| Adapter Temperature | 210 - 270 | °C | |
| Die Temperature | 210 - 270 | °C |
| Extrusion instructions |
|---|
| Feed Throat: 50 to 80°CZone 6: 220 to 270°CZone 7: 210 to 270°CZone 8: 210 to 270°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylite® ProCast PLUS 32144-40 | Reichhold Chemicals, Inc. | Polyester, TS | Polylite® ProCast PLUS |
| Xuchuan XCS-2043 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Geon™ Vinyl Flexible C6501 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| InnoGreen® BIO-80D | Innovative Polymers, Inc. | TSU | InnoGreen® |
| Sylvin 7844-95C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |