Order Products : sales@su-jiao.com
MAJORIS DG200
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OfG0dF_MAJORIS-DG200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DG200 is a 20% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in natural, but other colours can be provided on request. DG200 has been developed especially for demanding applications in various engineering sectors. DG200 has very high rigidity and impact strength, good dimensional stability and creep resistance also at high temperature. APPLICATIONS Product requiring, such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.1 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 76.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 34 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 144 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 133 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 161 | °C | ISO 306/A50 |
| -- | 126 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ A700 G20 H (f1) | PolyOne Corporation | Nylon 66 | Bergamid™ |
| KOPLA PP KPE1010 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |
| IPC PP 4832H-MLGF4-R2-UV | International Polymers Corporation | PP, Unspecified | IPC PP |
| Karina CLEAR PVC COMPOUND -E 85/243-DA-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 50/CF/7/GS/10/TF/5/EM/BK 100 | LEHVOSS Group | PC | LUVOCOM® |