Cleapact TS-50 E
| Category: | PS Alloy , Polystyrene Alloy |
| Manufacturer: | DIC Corporation |
| Trademark: | Cleapact |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Of4Vxx_Cleapact-TS-50-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CLEARPACT, developed by DIC's polymerization techniques, is a styrene-based copolymer resin with a superb balance between transparency and moldability. It has a lower water absorption rate when compared to acrylic resins. It can meet the varied needs of our customers in optical materials and daily goods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 71 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Injection Molded) | 64.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 3450 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 104 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 2.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Injection Molded) | 91.0 | % | JIS K7105 |
| Haze (Injection Molded) | 0.30 | % | JIS K7105 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 3.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND R3 | POLY GIN | PC | MARCOBLEND |
| Nipol® LX407F | Zeon Corporation | Latex | Nipol® |
| 3M™ Dyneon™ PTFE Compound TF 8615 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Hanwha Total PE 620L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |
| Kumho ABS HU650ZW | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |