RAMLLOY PN300G6
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMLLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OeYtG8_RAMLLOY-PN300G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE/PS ALLOY 30% GLASS FIBER RENFORCED FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/10.0 kg) | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.10 to 0.30 | % | ASTM D955 |
| -- | 0.10 to 0.30 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.20 | % | ASTM D570 |
| Saturation, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7900 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 90.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7300 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 130 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C | 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 145 | °C | |
| 1.8 MPa, Unannealed | 140 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 18 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Globalene® PC366-3 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| EPO-TEK® 920 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Iupiace® TX403 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Karina CLEAR PVC COMPOUND 66/200-DA-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina CLEAR PVC COMPOUND -E 80/278-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |