LNP™ VERTON™ RV00CESS compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Odd0k3_LNPVERTONRV00CESScompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* RV00CESS is a compound based on PA 66 resin containing Long Glass Fiber. Added features include: Easy Molding, Heat Stabilized. Also known as: LNP* VERTON* Compound RF70012EM Product reorder name: RV00CESS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 0.80 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.30 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 281 | MPa | ISO 527-2/5 |
| Fracture | 279 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 1.7 | % | ISO 527-2/5 |
| Fracture | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 19000 | MPa | ISO 178 |
| Flexural Stress | 418 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 3.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 52 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 95 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 255 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 252 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 288 - 299 | °C | |
| Processing (Melt) Temp | 288 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide AG8 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Aarolene® AVPS 100-3 | Aaron Industries Corp. | PS (HIPS) | Aarolene® |
| elitel UE3600 | UNITIKA Plastics Division | TPC-ET | elitel |
| LNP™ THERMOCOMP™ UF0037W compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| 3M™ Dyneon™ PTFE Compound TF 3215S | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |