ZYLAR® 960
| Category: | MMBS , Methyl Methacrylate Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | ZYLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Od12pK_ZYLAR-960.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ZYLAR 960 is an impact modified styrene acrylic copolymer that provides toughness equivalent to some grades of polycarbonate, good clarity and superior processing characteristics for demanding injection molded applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 200°C/5.0 kg | 6.00 | cm³/10min | |
| 220°C/10.0 kg | 65.0 | cm³/10min | |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.60 | % | ASTM D955 |
| -- | 0.20 to 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.10 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 62 | ASTM D785, ISO 2039-2 | |
| Ball Indentation Hardness | 35.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 1720 | MPa | ASTM D638 |
| -- | 1640 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 23.4 | MPa | ASTM D638 |
| Yield, 23°C | 28.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 70 | % | ASTM D638 |
| Break, 23°C | 120 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1720 | MPa | ASTM D790 |
| -- | 1640 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 42.7 | MPa | ASTM D790 |
| -- | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 23°C | 590 | J/m | ASTM D256 |
| 23°C | 15 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 200 | kJ/m² | ISO 180 |
| Gardner Impact | 19.2 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 78.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 86.1 | °C | |
| 1.8 MPa, Annealed | 67.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 93.9 | °C | ASTM D1525 1 |
| -- | 60.0 | °C | ISO 306/B50 |
| Maximum Service Temperature | 250 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | |||
| -- 2 | 1.570 | ASTM D542 | |
| -- | 1.560 | ISO 489 | |
| Transmittance (550 nm) | 91.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 30.0 to 55.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | Sodium D Line |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 4030 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Sinvicomp SBF5758 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| SWANCOR Epoxy 901-35 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Mafill® CR H 8044 P060 | Ravago Group | PP Homopolymer | Mafill® |
| Sylvin 8225-95UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |