Iupilon® EFT2200
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OcMbPK_Iupilon-EFT2200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon®EFT2200 is a polycarbonate (PC) material,. This product is available in North America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Iupilon®The main features of the EFT2200 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Vertical flow direction : 3.20mm | 0.50 - 0.70 | % | |
| Flow direction : 3.20mm | 0.50 - 0.70 | % | |
| Water Absorption (Saturation, 23°C) | 0.24 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 100 | % | ISO 527-2 |
| Flexural Modulus | 2350 | MPa | ISO 178 |
| Flexural Stress | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 70 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 136 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 125 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | UL 94 | |
| 2.00 mm | V-0 | UL 94 |
| Additional Information |
|---|
| EFT2200U: UV Stabilized |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 250 - 280 | °C | |
| Middle Temperature | 260 - 290 | °C | |
| Front Temperature | 270 - 300 | °C | |
| Nozzle Temperature | 270 - 300 | °C | |
| Mold Temperature | 70.0 - 100 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIMONA® PVC-C CORAN Industrial Grade | SIMONA AMERICA, Inc. | PVC, Rigid | SIMONA® |
| ACRYLITE® Sheet Resist 65 | Evonik Cyro LLC | Acrylic, Unspecified | ACRYLITE® Sheet |
| Colorite 88 Series 9588 | Colorite Polymers | PVC, Unspecified | Colorite 88 Series |
| Kepamid® 1320M7 | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| Innova R 970E | Innova SA | PS (HIPS) | Innova |