Synthos EPS® 0513F/PL
| Category: | PS (EPS) , Expanded Polystyrene |
| Manufacturer: | Synthos S.A. |
| Trademark: | Synthos EPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OcMBI1_Synthos-EPS-0513F-PL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Synthos EPS® F /PL type 0308F, 0513F, 0816F and 1325F is self-extinguishing expandable polystyrene EPS with high content of pentane. The materials are formed by spherical polystyrene particles that contain a flame retardant system (content of HBCD < 0,5%) and a hydrocarbon blowing agent. Their surface is treated against gluing during processing and the formation of electrostatic charge. Due to the content of halogenated flame retardant and the residual blowing agent, the product is unsuitable for objects intended for direct contact with food. Synthos EPS® 0513F/PL (Owipian FS 0513) is mainly used for production of shaped parts with wall thickness above 10 mm (e.g. shipping packaging for glass and electrical goods, building bricks, floor and roof shaped parts); production of smaller blocks with higher density or cutted profiles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | Internal Method | ||
| -- 1 | < 0.02 | g/cm³ | |
| -- 2 | 0.02 to 0.04 | g/cm³ | |
| Moisture Content | < 7000 | ppm | Internal Method |
| Particle Size - >95% between | 500 to 1250 | µm | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Reaction to Fire | |||
| -- | B1 | DIN 4102 | |
| -- | Class E | EN 13501-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blowing Agent | < 7.0 | wt% | Internal Method |
| Note Message | |
|---|---|
| 1 . | The laboratory tests of expanded beads bulk density are made according to Polish Standard PN-90/C-89298 using the following expansion times: 0308 and 0513: 12 min., 0816: 10 min., 1325: 6 min. |
| 2 . | The typical bulk density indicates values obtained during single-step pre-foaming on continuous pre-foaming devicesLower values of bulk density can be achieved only after multiple pre-expansion. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A 42 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| APEX® 3095-H | Teknor Apex Company | PVC, Flexible | APEX® |
| DENKA EVA TEX NA500 | Denka Company Limited | EVA | DENKA EVA TEX |
| Edgetek™ SF-10CF/000 BK001 | PolyOne Corporation | PPS | Edgetek™ |
| Eltex® MED 100-MG12 | INEOS Olefins & Polymers Europe | PP Homopolymer | Eltex® MED |