TRIBOCOMP® PA66 CF10 TS5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Oc7vcg_TRIBOCOMP-PA66-CF10-TS5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® PA66 CF10 TS5 is a Polyamide 66 (Nylon 66) product filled with 10% carbon fiber. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8100 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 252 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 3.0E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.40 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 270 to 300 | °C | |
| Front Temperature | 285 to 300 | °C | |
| Nozzle Temperature | 285 to 310 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 80.0 to 160 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A43^E F14 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Sinvicomp DBS3030 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Huaxia Shenzhou PVDF DS204 | Shandong Huaxia Shenzhou New Material Co., Ltd. | PVDF | Huaxia Shenzhou |
| Lumiplas® LD7650 | LG Chem Ltd. | PC | Lumiplas® |
| Plaslube® PC-50/TF/13/SI/2 NAT | Techmer Engineered Solutions | PC | Plaslube® |