AKROTEK® PEEK GF 40 natural (5068)
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROTEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ob9OAg_AKROTEK-PEEK-GF-40-natural-5068-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROTEK® PEEK GF 40 natural (5068) is a 40% glass fibre reinforced polyetheretherketone with very high stiffness and strength Applications are mainly elements in the automotive-, aeronautical-, industrial- and medical engineering that require high strength in a temperature environment above 150°C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.60 | g/cm³ | ISO 1183 |
| Spiral Flow | 63.0 | cm | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 14500 | MPa | ISO 178 |
| Flexural Stress 2 | 295 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 2.4 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 40 | % | ISO 1172 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 63 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 280 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 220 | °C | ISO 75-2/C |
| Melting Temperature 4 | 342 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6 PA-212 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| Compoceran E201 | Arakawa Chemical Industries, Ltd. | Epoxy | Compoceran |
| Exxtral™ Performance Polyolefin CMU201 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Kepex® 3830GF | Korea Engineering Plastics Co., Ltd | Polyester Alloy | Kepex® |
| POLYasa 2008F | Polykemi AB | ASA | POLYasa |