3M™ Dyneon™ Fluoroelastomer MIP 8640X is a dipolymer made from hexafluoropropylene and vinylidene fluoride. MIP 8640X has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Process targets: injection, compression and transfer moulding Proprietary incorporated cure technology Improved cure technology resulting in more consistent part size from successive moulding cycles Excellent barwelling / extrusion characteristics for fast and consistent preform production Improved scorch resistance at high moulding temperatures Excellent mould release - can be used in automated injection moulding equipment Clean running Typical Applications 3M™ Dyneon™ Fluoroelastomer MIP 8640X is suitable for the manufacture of O-rings produced in an injection moulding process.

Message

3M™ Dyneon™ Fluoroelastomer MIP 8640X is a dipolymer made from hexafluoropropylene and vinylidene fluoride. MIP 8640X has an incorporated bisphenol cure system.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Process targets: injection, compression and transfer moulding

Proprietary incorporated cure technology

Improved cure technology resulting in more consistent part size from successive moulding cycles

Excellent barwelling / extrusion characteristics for fast and consistent preform production

Improved scorch resistance at high moulding temperatures

Excellent mould release - can be used in automated injection moulding equipment

Clean running

Typical Applications
3M™ Dyneon™ Fluoroelastomer MIP 8640X is suitable for the manufacture of O-rings produced in an injection moulding process.

General Information
Features	Good demoulding performance
Uses	O-rings
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	43	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	78		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	7.80	MPa	ASTM D412A
Tensile Strength ²	15.0	MPa	ASTM D412A
Tensile Elongation ³(Break)	180	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	21	%	ASTM D1414
200°C, 70 hr ⁵	19	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
RTP 2185 HEC	RTP Company	PEI	RTP
TOTAL Polyethylene Lumicene® M 3410 EP (EU)	TOTAL Refining & Chemicals	MDPE	TOTAL Polyethylene
UNISOFT TPE™ ST-40A-CL-1-01	UNITED SOFT PLASTICS, Inc.	SEBS	UNISOFT TPE™
Karina BLACK PVC COMPOUND 902-48/1-IS (*)	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Durethan® BKV 40 000000	LANXESS Corporation	Nylon 6	Durethan®