VITAMIDE® AT36NT6214
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OaXy06_VITAMIDE-AT36NT6214.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® AT36NT6214 is a Polyamide 66 (Nylon 66) product filled with 20% glass fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 95.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5400 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 180 | MPa | ISO 178 |
| Break | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 1 | 46.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 46 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 250 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 34 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 450 | V | IEC 60112 |
| -- 2 | 450 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 23 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method A |
| 2 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® S SG4 | Nanjing Julong Engineering Plastics Co., LTD | ABS | Wondel® S |
| Westlake HDPE MC2004 | Westlake Chemical Corporation | HDPE | Westlake HDPE |
| ASI POLYPROPYLENE 984 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| ENLIGHT™ 4145F | The Dow Chemical Company | Polyolefin, Unspecified | ENLIGHT™ |
| Jiangsu Sinarise PI90001X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |