DOW™ Electrical & Telecommunications DGDA-1310 BK

Category:	HDPE , Black High Density Polyethylene Compound for Cable Jacketing
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ Electrical & Telecommunications
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	OYnCoB_DOW-Electrical-Telecommunications-DGDA-1310-BK.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DGDA-1310 BK is a black HDPE jacket grade for power and telecom cable applications. The material provides excellent mechanical and physical properties and environmental stress crack resistance in combination with good processability.

DGDA-1310 BK can be extruded using conventional cable jacket techniques with melt temperatures typically between 200 and 230 °C.

Specifications.
DGDA-1310 BK meets the following Raw material specifications:

ASTM D 1248 Type III, Class C, Category 5, Grade J4, E8, E9, W8, W9

ISO 1872-PE, KHL, 50-D003

Cables jacketed with DGDA-1310 BK, using industry standard commercial extrusion practice, should meet the following cable specifications:

IEC 60502, ST 7

IEC 62067, ST 7

IEC 60840, ST 7

ICEA S-94 649

ICEA S-108 720

ICEA S-97 682

ICEA-S-87-640

BS 6234: Type H03C, TS2

Telcordia GR-70-CORE

HD 620 S2, Part 1, Table 4B, type DMP2, DMP 9-10, DMP 14-15, DMP 17

EN 50290-2-24

General Information
Agency Ratings	ASTM D 1248, III, Class C, Cat. 5 Grade J4, E8, E9, W8, W9 BS 6234 Type H03C, TS2 EN 50290-2-24 HD 620 S2, Part 1, Table 4B, type DMP2, DMP 9-10, DMP 14-15, DMP 17 ICEA S-108-720 ICEA S-87-640 ICEA S-94-649 ICEA S-97-682 IEC 60502 Type ST7 IEC 60840 Type ST7 IEC 62067 Type ST7 ISO 1872 PE KHL 50D003
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.965	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR)			ASTM D1238, ISO 1133
190°C/2.16 kg	0.26	g/10 min
190°C/21.6 kg	28	g/10 min
Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F0)	> 1000	hr	IEC 60811
Carbon Black Content	2.5	%	ASTM D1603
Absorption Coefficient	445 K(AB/M)		ASTM D3349

Aging	Nominal Value	Unit	Test Method
Retention of Tensile Elongation - 14 days (110°C)	93	%	IEC 60811
Retention of Tensile Strength - 14 days (110°C)	93	%	IEC 60811

Thermal	Nominal Value	Unit	Test Method
Oxidation Induction Time (200°C)	170	min	ASTM D3895

Hardness	Nominal Value	Unit	Test Method
Shore Hardness			ISO 868
Shore D, 1 sec	66
Shore D, 3 sec	63

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	29.0	MPa	IEC 60811
Tensile Elongation (Break)	820	%	IEC 60811
Flexural Modulus	1180	MPa	ISO 178
Taber Abrasion Resistance (100 Cycles)	21.0	mg	ASTM D1242

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature ¹	-76.0	°C	ASTM D746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity (23°C)	5.6E+16	ohms·cm	ASTM D257

Note Message
1 .	No Failure

Resin Grade	Manufacturer	Category	Trademark
RTP 1005 FR A	RTP Company	PBT	RTP
Spartech Polycom SC14F-1060L	Spartech Polycom	Nylon 66	Spartech
Texalan® 6 Series 672D	Austin Novel Materials Co. Ltd.	TPU-Ester/Ether	Texalan® 6 Series
Hydrin® T3102	Zeon Chemicals L.P.	Epoxy	Hydrin®
Karina WHITE PVC COMP E 880-10/136-A-IS-AS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina