RELENE® F56003
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OYbc4S_RELENE-F56003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| F56003 is a High Density Polyethylene (HDPE) grade suitable for producing blown film with excellent drawdown and paper like feel. It is recommended for making carrier bags and co-extruded film structures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 40 µm, Blown Film | 35.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 37.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 55.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 50.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 700 | % | |
| TD : Break, 40 µm, Blown Film | 900 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 64 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm, Blown Film | 28 | g | |
| TD : 40 µm, Blown Film | 400 | g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 454N | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| Vi-Chem PVC VNC87-80E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| FHR Polypropylene P4G4B-036 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Gallonprene® GP520-7509 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina WHITE PVC COMPOUND -E 813-10/164-B-RT-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |