Sumitomo PE FS250B
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Sumitomo Chemical Asia |
| Trademark: | Sumitomo PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OYGvLq_Sumitomo-PE-FS250B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Applications For cast stretch film, lamination film, wire and cable, and general purpose film applications. Characteristics:HighStrength, tough, and easy processability transparent cast film. Also used for wire and cable and high strength blown film, non-- slip with excellent processability. For higher transparency, blending with LDPE is recommended. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Static) | > 0.51 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | |||
| -- 1 | 20 | µm | |
| -- 2 | 30 | µm | |
| Secant Modulus - 1% Secant, MD | ASTM D882 | ||
| -- 3 | 205 | MPa | ASTM D882 |
| -- 4 | 150 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, blown film | 35.0 | MPa | ASTM D882 |
| MD : Fracture, extruded film | 50.0 | MPa | ASTM D882 |
| TD : Broken, blown film | 30.0 | MPa | ASTM D882 |
| TD : Fracture, extruded film | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, blown film | 770 | % | ASTM D882 |
| MD : Fracture, extruded film | 620 | % | ASTM D882 |
| TD : Broken, blown film | 930 | % | ASTM D882 |
| TD : Fracture, extruded film | 940 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709 | ||
| Blow film | 90 | g | ASTM D1709 |
| Cast film | 75 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : Blow film | 130 | g | ASTM D1922 |
| MD : cast film | 60 | g | ASTM D1922 |
| TD : Blow film | 350 | g | ASTM D1922 |
| TD : cast film | 240 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 122 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45, blown film | 50 | ASTM D2457 | |
| 45, cast film | 145 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| Blow film | 20 | % | ASTM D1003 |
| Cast film | 0.60 | % | ASTM D1003 |
| Additional Information |
|---|
| Cast film fabrication: extruder 55mm, die width 600mm, die gap 1.2mm, extrusion temperature 280°C, chill roll 30°C, output 50kg/hr, line speed 75m/min, thickness 20µm.Blown film processing condition: extruder ø55mm, die ø125mm, die gap 2.0mm, temperature 200°C, output 30kg/hr, blow-up ratio 2.0, thickness 30µm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 280 | °C |
| Note Message | |
|---|---|
| 1 . | Cast |
| 2 . | Blown |
| 3 . | Blown |
| 4 . | Cast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A33^E | Polykemi AB | Nylon 66 | SCANAMID 66 |
| TPC PVC SM71E | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| AIE PPO 9010F-S115D | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| EVATHENE® UE638-04 | USI Corporation | EVA | EVATHENE® |
| EMOPLEN® AR 1205 RT2 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |