LNP™ STAT-KON™ RE004 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OXHD9e_LNP-STAT-KON-RE004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON RE004 is a compound based on Nylon 66 resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound RC-1004 Product reorder name: RE004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break | 219 | MPa | ASTM D638 |
| Break | 233 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 4.3 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 12300 | MPa | ASTM D790 |
| -- | 14600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 312 | MPa | ASTM D790 |
| -- | 337 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 1 | 8.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 520 | J/m | ASTM D4812 |
| 23°C 2 | 55 | kJ/m² | ISO 180/1U |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN HIP-372 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| NEXUS Reprocessed HDPE 8/960 RBK | Nexus Resin Group, LLC. | HDPE | NEXUS Reprocessed |
| Fiberfil® J-60/30/E5 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| HIFOR Xtreme® SC74836 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |
| Sylvin 6177-80 Orange 597 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |