Eraclene® MP 90 C
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OWCq3z_Eraclene-MP-90-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene MP 90 C is a gas phase high density polyethylene homopolymer resin (HDPE) with antioxidants, suitable for injection moulding application. This grade has a narrow molecular weight distribution and a high density that make it ideally for injection moulding applications where outstanding rigidity, warp resistance and toughness are required. The polymer has high purity and high thermal stability during extrusion Main Application Eraclene MP 90 C has controlled organoleptic properties for the production of caps for PET bottles used for natural mineral water, fruit juice, etc. Eraclene MP 90 C is suitable to produce moulded crates with requiring rigidity. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 8.0 | g/10 min | |
| 190°C/5.0 kg | 21 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 69 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 30.0 | MPa | |
| Break, Compression Molded | 17.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | 400 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 1450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(Compression Molded) | 100 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ISO 306/A |
| Melting Temperature | 137 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 260 | °C | |
| Middle Temperature | 190 to 260 | °C | |
| Front Temperature | 190 to 260 | °C | |
| Mold Temperature | 10.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAPPO™ J910 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| Vydyne® R533H BK0201 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Europrene® SOL T 9326 | Versalis S.p.A. | SIS | Europrene® |
| Fainplast PVC PM 5010 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| OTECH PVC OC7018-Soles | OTECH Corporation | PVC, Unspecified | OTECH PVC |