Celanex® 3209HR
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OVr5iR_Celanex-3209HR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 3209HR is a 15% glass filled PBT that has an excellent hydrolysis resistance, mechanical properties and processability. Celanex 3209HR is non-lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.90 | % | ISO 294-4 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.17 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 5300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 22 | kJ/m² | ISO 179/1eU |
| 23°C | 22 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 5.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 17 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 180 | °C | ISO 75-2/A |
| Glass Transition Temperature | 60.0 | °C | ISO 11357-2 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 4.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.70 | IEC 60250 | |
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.024 | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw Speed: Medium |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 612 GF 30 H | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| Styropor® P-440H | BASF Corporation | PS (EPS) | Styropor® |
| NYCOA NanoSEAL™ NS-80-100 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA NanoSEAL™ |
| InnoClear™ OC-7086 | Innovative Polymers, Inc. | TSU | InnoClear™ |
| Polidan® PNT 0555/06 | Solvay Specialty Polymers | XLPE | Polidan® |